Industries
Cement
Food Processing
Locomotive [Trains]
Marine / offshore
Material Handling
Metal Forming [Press / Forge]
Mining, Quarries - Mineral processing
Petrochemical / refinery
Plastic
Power station / generation
Printing
Pulp & Paper
Reconditioners
Steel Industry
Sugar
Tyre industry [Rubber manufacturing]
Vintage / Heritage
Wire & Cable
 
Typical Applications
Compressors
Electric Motors
Engines/Cylinder Blocks
Gearboxes / casings
Generators
Pumps
 
 
     
 
Introduction Sitemap
 
     
 
Metalock Quote
 
     
 


View Metalock in a larger map
 
USED EQUIPMENT
 


Cast Repairs, Onsite Machining, Specialized Welding, Engineering, Jobbing / Manufacturing

The Metalock process is a unique cold engineering method of repairing fractures or damage to all types of castings. Especially for cast iron/steel as these materials are difficult, risky and costly to repair via welding. We provide cost effective/problem solving through utilisation of leading edge technology and training. Our ability to create innovative solutions and see them through in a timely and responsive manner is your "key to service."

History of Metalock

Metalock originated in the oil fields of Texas in the mid 1930's to overcome the explosive potential of welding repairs. A system was developed which eliminated heat, and had many ancillary advantages, including the elimination of distortion, which in turn obviated re-machining in most cases. Subsequent development by the U.S.A. defence forces during WWII were responsible for the spread of this technology and its acceptance in heavy industries.

Further development in the 1950's led to the establishment of the Metalock International Association. MIA Conferences are held once a year in various parts of the world, so members can update techniques, evaluate R&D and extend the services offered.




What is Metalock?

Technically the Metalock method is very simple. A crack in a cast component is locked using a key which takes up both tensile and compressive stresses. Screws are driven in along the crack in order to take up shear stresses.

During the repair the metal actually "flows" with peening to fill the whole of the aperture which compensates for the slight imperfections due to drilling. The keys are very accurately formed to ensure a very good fit in the apertures.

It is possible to determine the tensile strength lost when a casting is fractured and we are able to accurately calculate the amount of strength restored by the Metalock keys.

The apertures for the keys are prepared at set centers and at right angles to and across the line of the fracture to the exact female form of the Metalock keys. The accuracy of this work relies mainly on the experience and craftsmanship of the Metalock engineer although he does make use of certain jigs and fixtures.

Material Used In Metalock Process

The material used in the Metalock process is a corrosion resistant Nickel Alloy. The advantages this material has is its ductility in the annealed condition, giving reasonable tensile strength when work hardened, a low rate of strain hardening and a very low coefficient of thermal expansion, similar to cast iron.

Variations Of The Metalock Process

Masterlocks are often used in conjunction with the Metalock process, in points of high stress concentration or in sections subject to overloading and subsequent fracture. They are comprised of inlays of high strength alloy plate held in place by dowels, cold worked into matching half holes between the parent material and the alloy plate. The Masterlocks vary in size, shape and even material, dependant upon requirements of each repair.